Users should evaluate the suitability of this product for their application. Specifications are subject to change without notice.
Tyco Electronics Corporation also reserves the right to make changes in materials or processing, which do not affect compliance with any specification, without notification to Buyer.
1/ COLORS AND COLOR CODE DESIGNATORS SHALL BE IN A CCORDANCE WITH MIL-STD-681. OTHER CODES AND SUFFIXES MAY BE
ADDED TO THE PART NUMBER, AS NECESSARY, TO CAPTURE ANY ADDITIONAL REQUIREMENTS IMPOSED BY THE PURCHASE ORDER.
Page 1 of 2
Raychem, TE Connectivity, TE connectivity (logo), and TE (logo) are trademarks.
Raychem Wire & Cable
501 Oakside Avenue
Redwood City, CA 94063-3800
Phone: 1-800-227-8816
Fax: 1-650-361-6297
DIMENSIONS ARE IN INCHES AND, UNLESS OTHERWISE DESIGNATED, ARE NOMINAL.
THIS SPECIFICATION SHEET TAKES PRECEDENCE OVER DOCUMENTS REFERENCED HEREIN.
REFERENCED DOCUMENTS SHALL B E OF THE ISSUE IN EFFECT ON DATE OF INVITATION FOR BID.
© 2015-2016 Tyco Electronics Corporation. All rights reserved.
Title SPECIFICATION CONTROL DRAWING SCD 400R0111
WIRE, RADIATION-CROSSLINKED, POLYOLEFIN-INSULATED, LIMITED FIRE HAZARD, 600 VOLT Date 3-8-16 Revision B
This specification sheet forms a part of the latest issue of Raychem Specification WCD 3114.
PRIMARY INSULATION - RADIATION-CROSSLINKED,
POLYOLEFIN
CONDUCTOR - TIN-COATED COPPER JACKET - RADIATION-CROSSLINKED,
FLUOROPOLYMER
Thickness: .003 ± .001 in.
(.051 mm min, .102 mm max)
TABLE I. CONSTRUCTION DETAILS
PART NUMBER
1/
WIRE
SIZE
(AWG)
CONDUCTOR
STRANDING
(number x AWG)
DIAMETER OF
STRANDED CONDUCTOR
(inch) (mm)
FINISHED WIRE
MAXIMUM
RESISTANCE
AT 20°C
(ohms/1000 ft.)
(ohms/km)
DIAMETER
(inch) (mm) MAXIMUM
WEIGHT
(lbs/1000 ft.)
(kg/km)
MINIMUM MAXIMUM MINIMUM MAXIMUM
400R0111-26-* 26 19 x 38 .018 (.457) .021 (.533) 41.3 (135.) .032 (.813) .036 (.914) 1.4 (2.08)
400R0111-24-* 24 19 x 36 .023 (.584) .026 (.660) 26.2 (86.0) .038 (.965) .042 (1.07) 2.0 (2.98)
400R0111-22-* 22 19 x 34 .029 (.737) .033 (.838) 16.2 (53.1) .045 (1.14) .049 (1.24) 3.0 (4.46)
400R0111-20-* 20 19 x 32 .037 (.940) .041 (1.04) 9.88 (32.4) .053 (1.35) .057 (1.45) 4.5 (6.70)
400R0111-18-* 18 19 x 30 .046 (1.17) .051 (1.30) 6.23 (20.4) .063 (1.60) .067 (1.70) 6.8 (10.1)
400R0111-16-* 16 19 x 29 .052 (1.32) .058 (1.47) 4.81 (15.8) .069 (1.75) .075 (1.91) 8.6 (12.8)
400R0111-14-* 14 19 x 27 .065 (1.65) .073 (1.85) 3.06 (10.0) .085 (2.16) .093 (2.36) 13.2 (19.6)
400R0111-12-* 12 37 x 28 .084 (2.13) .090 (2.29) 2.02 (6.63) .104 (2.64) .112 (2.84) 20.2 (30.1)
400R0111-10-* 10 37 x 26 .106 (2.69) .114 (2.90) 1.26 (4.13) .125 (3.18) .133 (3.38) 31.1 (46.3)
SPECIFICATION CONTROL DRAWING Page
2 of 2
Revision
B
SCD
400R0111
TABLE II. PERFORMANCE DETAILS
PART NUMBER
1/
BEND TESTING
MANDREL DIAMETER
(inch) (mm) (± 3%) WEIGHT
(lb) (kg) (± 3%)
ACCELERATED
AGING COLD
BEND ACCELERATED
AGING COLD
BEND
400R0111-26-* .500 (12.7) .500 (12.7) .250 (.113) .500 (.227)
400R0111-24-* .500 (12.7) .500 (12.7) .375 (.170) .500 (.227)
400R0111-22-* .750 (19.1) .750 (19.1) .375 (.170) 1.00 (.454)
400R0111-20-* .750 (19.1) .750 (19.1) .375 (.170) 1.00 (.454)
400R0111-18-* 1.00 (25.4) 1.00 (25.4) .500 (.227) 1.00 (.454)
400R0111-16-* 1.00 (25.4) 1.00 (25.4) .500 (.227) 1.00 (.454)
400R0111-14-* 1.50 (38.1) 1.50 (38.1) 1.00 (.454) 3.00 (1.36)
400R0111-12-* 2.00 (50.8) 2.00 (50.8) 1.00 (.454) 3.00 (1.36)
400R0111-10-* 2.50 (63.5) 2.50 (63.5) 1.00 (.454) 3.00 (1.36)
WIRE RATINGS AND ADDITIONAL REQUIREMENTS
TEMPERATURE RATING: 125°C
Maximum continuous conductor temperature
VOLTAGE RATING: 600 volts (rms) at sea level
ACCELERATED AGING: 300 ± 2°C for 6 hours
Identification legibility, 225 ± 2°C for 6 hours
BLOCKING: 150 ± 2°C for 24 hours
COLOR: White preferred
FLAMMABILITY: Char Length, 5 ft. (1.5 m) (maximum)
HUMIDITY RESISTANCE: Insulation Resistance,
5000 megohms for 1000 ft. (1524 megohms for 1 km) (minimum)
INSULATION ELONGATION AND TENSILE STRENGTH:
Primary Insulation,
Elongation, 150% (minimum)
Tensile Strength, 2500 lbf/in2 (17.2 MPa) (minimum)
INSULATION FLAWS:
Primary Insulation,
Spark Test, 1.5 kV (rms)
Impulse Dielectric Test, 6.0 kV (peak)
Finished Wire,
Spark Test, 3.0 kV (rms) at 3 kHz
Impulse Dielectric Test, 8.0 kV (peak)
INSULATION RESISTANCE:
5000 megohms for 1000 ft. (1524 megohms for 1 km) (minimum)
LOW TEMPERATURE-COLD BEND: -65 ± 2°C for 4 hours
SHRINKAGE: 300 ± 2°C, 0.125 in. (3.18 mm) (maximum) in 12 inches (305 mm)
SMOKE RELEASE:
Peak Smoke Release Rate, 0.40 m2/s (maximum)
Total Smoke Release, 150 m2 (maximum)
SMOKE TEST: D4, 50 (maximum); Dm, 300 (maximum)
TOXICITY: HCN: 100 ppm (maximum) SO2: 100 ppm (maximum)
CO: 3500 ppm (maximum) HF: 100 ppm (maximum)
NO: 100 ppm (maximum) HCI: 500 ppm (maximum)
VOLTAGE WITHSTAND (Post Environmental): 2500 volts (rms), 60 Hz, 5 minutes
1/ PART NUMBER:
The "*" in the part numbers in Tables I and II shall be replaced by a color code
designator.
Example: AWG 20, white: 400R0111-20-9
AWG 20, white with a black stripe: 400R0111-20-90
PRODUCT IDENTIFICATION:
Outer surface of wire shall be marked in contrasting color as follows:
"RAYCHEM 400R0111-xx - 600V Yr of Mfg" (xx = applicable AWG size)