Scotch-WeldTM Epoxy Adhesive DP100 Plus Clear Technical Data Product Description September 2016 3MTM Scotch-WeldTM Epoxy Adhesive DP100 Plus Clear is a fast setting, two-part, 1:1 mix ratio mercaptan-cured epoxy adhesive. It is unique among fast setting mercaptan cure epoxies in that it combines high shear strength with good peel performance properties. Scotch-Weld Epoxy adhesive DP100 Plus Clear is transparent and slightly flexible when cured. Available in bulk containers as 3MTM Scotch-WeldTM Epoxy Adhesive DP100 Plus B/A Clear. Features Typical Uncured Physical Properties * 4 minute worklife * High shear and peel strength * Slightly flexible * 1:1 mix ratio Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. BASE RESINS Epoxy/Mercaptan Viscosity1 Approximate @ 80F (23C) Base (B) Accelerator (A) Net Weight (Lbs./Gallon) Base (B) Accelerator (A) 9.7 to 9.9 9.4 to 9.8 Color2 Base (B) Accelerator (A) Clear Clear Mix Ratio (B:A) By Volume By Weight Worklife3 @ 73F (23C) 2 gram 20 gram 4,000 to 11,000 cps 7,000 to 13,000 cps 1:1 1:1 4 min. 3 min. Viscosity determined using test method C-1d. Procedure involves Brookfield RVF, #7 spindle, 20 rpm and 80F (27C). Measurement taken after 1 minute revolution. 2 Color may vary from colorless to yellow/amber. Adhesive performance is not affected by color variation. 3 Worklife determined using test method C-3180. Procedure involves periodically measuring a 2 gram mixed mass for self leveling and wetting properties. This time will also approximate the usable worklife in an 3MTM EPXTM Applicator mixing nozzle. 1 3MTM Scotch-WeldTM Epoxy Adhesive DP100 Plus Clear Typical Cured Properties Note: The following technical information and data should be considered representative or typical only and should not be used for specification purposes. PHYSICAL Color Clear Hardness (ASTM D 2240) Shore D 65-70 Worklife 2 3-4 minutes 3 9-10 minutes Tack-free Time 4 20 min. @ 73F (23C) Time to Handling Strength Cure Time 5 48 hrs. @ 73F (23C) 6 75% Elongation 6 1850 psi Tensile Strength THERMAL Weight Loss by Thermal Gravimetric Analysis (TGA) 8 7 1% @ 116C 5% @ 318C -6 Thermal Coefficient of Expansion (TCE) by TMA ( x 10 units/unit/C) Below Tg Above Tg 93 (5-20C range) 182 (40-140C range) 9 Glass Transition Temperature (Tg) by DSC Onset Mid-Point 23C 29C 10 Thermal Conductivity (@ 110F on2 .250" samples) BTU - ft./ft. - hr. - F Cal./sec. - cm - C Watt/m - C 11 Thermal Shock Resistance Potted Washer Olyphant Test (Test Method C-3174 + 100C [air] to -50C [liquid]) .077 -3 .32 x 10 .133 Pass 5 cycles without cracking ELECTRICAL Dielectric Constant @ 1 KHz @ 23C (ASTM D 150) 6.6 Dissipation Factor @ 1 KHz @ 23C (ASTM D 150) 0.06 710 volts/mil Dielectric Strength (ASTM D 149) Sample Thickness Approx. 30 mil. 11 Volume Resistivity (ASTM D 257) 6.7 x 10 ohm-cm 2 Worklife determined using test method C-3180. Procedure involves periodically measuring a 2 gram mixed mass for self leveling and wetting properties. This time will also approximate the usable worklife in an 3MTM EPXTM Applicator mixing nozzle. 3 Tack-free time determined per test method C-3173. Involves dispensing 0.5 gram amount of adhesive onto substrate and testing periodically for no adhesive transfer to metal spatula. 4 Handling strength determined per test method C-3179. Time to handling strength taken to be that required to achieve a 50 psi overlap shear (OLS) strength using aluminum substrates. 5 The cure time is defined as that time required for the adhesive to achieve a minimum of 80% of the ultimate strength as measured by aluminum- aluminum OLS. 6 Tensile and Elongation. Used procedure in test method C-3094/ATSM D 882. Samples were 2 in. dumbbells with .0125 in. neck and .030 in. sample thickness. Separation rate was 2 inches per minute. Samples cured 2 hrs. RT plus 2 hrs. 160F (71C). 7 Weight loss by TGA reported as that temperature at which 5% weight loss occurs by TGA in air at 5C rise per minute per ASTM 1131-86. 8 TCE determined using TMA Analyzer using a heating rate of 10C per minute. Second heat values given. 9 Glass Transition Temperature (Tg) determined using DSC Analyzer with a heating rate of 20C per minute. Second heat values given. 10 Thermal conductivity determined using ASTM C177 and C-matic Instrument using 2 in. diameter samples. 11 Thermal shock resistance run per test method C-3174. Involves potting a metal washer into a 2 in. x 0.5 in. thick section and cycling this test specimen to colder and colder temperatures. 2 3MTM Scotch-WeldTM Epoxy Adhesive DP100 Plus Clear Typical Adhesive Performance Characteristics Note: The following product performance data was obtained in the 3M laboratory under the conditions specified. The following data show typical results obtained with 3MTM Scotch-WeldTM Epoxy Adhesive DP100 Plus Clear when applied to properly prepared substrates, cured, and tested according to the specifications indicated. This data was generated using the 3MTM EPXTM Applicator System equipped with an EPX static mixer, according to manufacturer's directions. Thorough hand mixing should afford comparable results. 12 Overlap Shear Strength (OLS) to (Bonds cured 24 hours @ room temperature (RT) + 2 hrs @ 160F [71C]) Etched Aluminum 3500 psi Sanded Aluminum (60 grit) 1800 psi Cold Rolled Steel 1700 psi Wood, Fir 700 psi Glass, Borosilicate 250 psi Glass, +3MTM Scotch-WeldTM Primer EC3901 300 psi Polycarbonate 600 psi Acrylic 300 psi Fiberglass 1500 psi ABS 280 psi PVC 450 psi Polypropylene 80 psi Rate of Strength Buildup 12 (OLS on Etched Aluminum) Bonds tested after: 1 hr @ RT 600 psi 6 hrs @ RT 900 psi 24 hrs @ RT 1100 psi 7 days @ RT 2800 psi 1 mo @ RT 3400 psi Environmental Aging 12 (OLS on Etched Aluminum) Bonds tested after: 24 hrs RT + 2 hrs @ 160F (71C) 12 3500 psi 24 hrs RT + 2 hrs @ 240F (116C) 4500 psi 1 wk RT + 1 wk @ 90F (32C)/90% RH 3900 psi 1 wk RT + 1 wk 248F (120C) 4500 psi 1 wk RT + 1 wk H2O immersion 3500 psi Overlap shear (OLS) strengths were measured on 1 in. wide 1/2 in. overlap specimens. These bonds were made individually using 1 in. x 4 in. pieces of substrate. The thickness of the bond line was 0.005-0.008 in. All strengths were measured at 70F (21C) except where noted. (Test per ASTM D 1002-72.) The separation rate of the testing jaws was 0.1 in. per minute for metals, 2 in. per minute for plastics and 20 in. per minute for rubbers. The thickness of the substrates were: steel, 0.060 in.; other metals, 0.05-0.064 in.; rubber, 0.125 in.; plastics, 0.125 in. 3 3MTM Scotch-WeldTM Epoxy Adhesive DP100 Plus Clear Typical Adhesive Performance Characteristics (continued) 12 Overlap Shear Strength (OLS) vs. Temperature, Etched Aluminum (Bonds cured 24 hours @ room temperature (RT) + 2 hours @ 160F [71C]) Bonds tested at: -67F (-55C) 3000 psi 70F (21C) 3500 psi 120F (49C) 750 psi 150F (66C) 400 psi 180F (82C) 200 psi 13 180 Peel Strength vs. Temperature, Etched Aluminum (Bonds cured 24 hours @ room temperature (RT) + 2 hours @ 160F [71C]) -67F (-55C) 2 piw 70F (21C) 13 piw 120F (49C) 15 piw 150F (66C) 2 piw 180F (82C) 1 piw 14 Solvent Resistance One Hour/One Month Acetone A/A Isopropyl Alcohol A/A Freon TF A/A Freon TMC A/A 1,1,1-Trichloroethane A/A RMA Flux A/A Key: A - Unaffected, B - Slight Attack, C - Moderate/Severe Attack 15 Exotherm Max. Temp/Time to Reach 12 2 gram mass 128F/6 min. 20 gram mass 260F/3 min. Overlap shear (OLS) strengths were measured on 1 in. wide 1/2 in. overlap specimens. These bonds were made individually using 1 in. x 4 in. pieces of substrate. The thickness of the bond line was 0.005-0.008 in. All strengths were measured at 70F (21C) except where noted. (Test per ASTM D 1002-72.) The separation rate of the testing jaws was 0.1 in. per minute for metals, 2 in. per minute for plastics and 20 in. per minute for rubbers. The thickness of the substrates were: steel, 0.060 in.; other metals, 0.05-0.064 in.; rubber, 0.125 in.; plastics, 0.125 in. 13 T-peel strengths were measured on 1 in. wide bonds at 73F (23C). The testing jaw separation rate was 20 inches per minute. The substrates were 0.020 in. thick. (Tests per ASTM D 1876-61T.) 14 Solvent resistance was determined using cured (24 hrs. RT + 2 hrs. 160F [71C]) samples (1/2 in. x 4 in. x 1/8 in. thickness) immersed in the test solvent for 1 hour and 1 month. After the allotted period of time, the sample was removed and visually examined for surface attack as compared to the control. Key: A - Unaffected - no change to color or surface texture. B - Slight attack - noticeable swelling of surface. C - Moderate/severe attack - extreme swelling of surface. 15 Exotherm determined using the stated mass mixed for 1 minute and then by electronic thermocouple measuring the peak temperature and time to that temperature. 4 3MTM Scotch-WeldTM Epoxy Adhesive DP100 Plus Clear 3MTM EPXTM Pneumatic Applicator Delivery Rates 400 ml Applicator - Maximum Pressure 73 psi Adhesive* 3MTM Scotch-WeldTM Epoxy Adhesive DP100 Plus Clear 6mm Nozzle gms/minute 10mm Nozzle gms/minute 54 206.5 45.7 179 200 ml Applicator - Maximum Pressure 58 psi 3MTM Scotch-WeldTM Epoxy Adhesive DP100 Plus Clear 50 ml Applicator - Maximum Pressure 50 psi 1/4 in. Nozzle gms/minute Adhesive* 3MTM Scotch-WeldTM Epoxy Adhesive DP100 Plus Clear 60 *Tests were run at a temperature of 70F 2F (21C 1C) and at maximum applicator pressure. Application Equipment Suggestions For small or intermittent applications, the 3MTM EPXTM Applicator is a convenient method of application. For larger applications, these products may be applied by use of flow equipment. Two-part meter/mixing/dispensing equipment is available for intermittent or production line use. These systems may be desirable because of their variable shot size and flow rate characteristics and are adaptable to many applications. 5 3MTM Scotch-WeldTM Epoxy Adhesive DP100 Plus Clear Handling/Curing Information Directions For Use 1. For high strength structural bonds, paint, oxide films, oils, dust, mold release agents and all other surface contaminants must be completely removed. However, the amount of surface preparation depends on the required bond strength and the environmental aging resistance desired by user. For specific surface preparations on common substrates, see the section on surface preparation. 2. Use gloves to minimize skin contact. Do not use solvents for cleaning hands. 3. Mixing: For Duo-Pak Cartridges 3MTM Scotch-WeldTM Epoxy Adhesive DP100 Plus Clear is supplied in a dual syringe plastic duo-pak cartridge as part of the 3MTM EPXTM Applicator System. To use, simply insert the duo-pak cartridge into the EPX applicator and start the plunger into the cylinders using light pressure on the trigger. Next, remove the duo- pak cartridge cap and expel a small amount of adhesive to ensure both sides of the duo-pak cartridge are flowing evenly and freely. If automatic mixing of Part A and Part B is desired, attach the EPX applicator mixing nozzle to the duo-pak cartridge and begin dispensing the adhesive. For hand mixing, expel the desired amount of adhesive and mix thoroughly. Mix approximately 15 seconds after uniform color is obtained. For Bulk Containers Mix thoroughly by weight or volume in the proportions specified in the typical uncured properties section. Mix approximately 15 seconds after uniform color is obtained. 4. For maximum bond strength, apply adhesive evenly to both surfaces to be joined. 5. Application to the substrates should be made within 3 minutes. Larger quantities and/or higher temperatures will reduce this working time. 6. Join the adhesive coated surfaces and allow to cure at 60F (16C) or above until completely firm. Heat up to 200F (93C), in order to speed curing. These products will cure in 48 hours @ 75F (24C). 7. Keep parts from moving during cure. Contact pressure necessary. Maximum shear strength is obtained with a 3-5 mil bond line. 8. Excess uncured adhesive can be cleaned up with methyl ethyl ketone (MEK).* Adhesive Coverage: A 0.005 in. thick bond line will yield a coverage of 320 sq. ft./gallon. *Note: When using solvents, extinguish all ignition sources, including pilot lights, and follow manufacturer's precautions and directions for use. 6 3MTM Scotch-WeldTM Epoxy Adhesive DP100 Plus Clear Surface Preparation For high strength structural bonds, paint, oxide films, oils, dust, mold release agents and all other surface contaminants must be completely removed. However, the amount of surface preparation directly depends on the required bond strength and the environmental aging resistance desired by user. The following cleaning methods are suggested for common surfaces: Steel Wipe free of dust with oil-free solvent such as acetone, isopropyl or alcohol solvents.* Sandblast or abrade using clean fine grit abrasives. Wipe again with solvent to remove loose particles. If a primer is used, it should be applied within 4 hours after surface preparation. 1. 2. 3. 4. Aluminum 1. Alkaline Degrease: Oakite 164 solution (9-11 oz./gallon water) at 190F 10F (88C 5C) for 10-20 minutes. Rinse immediately in large quantities of cold running water. 2. Acid Etch: Place panels in the following solution for 10 minutes at 150F 5F (66C 2C). Sodium Dichromate 4.1 - 4.9 oz./gallon Sulfuric Acid, 66Be 38.5 - 41.5 oz./gallon 2024-T3 aluminum (dissolved) 0.2 oz./gallon minimum Tap water as needed to balance 3. Rinse: Rinse panels in clear running tap water. 4. Dry: Air dry 15 minutes; force dry 10 minutes at 190F 10F (88C 5C). 5. If primer is to be used, it should be applied within 4 hours after surface preparation. Note: Read and follow component supplier's environmental health and safety information prior to preparing this etch solution. Plastics/Rubber 1. Wipe with isopropyl alcohol.* 2. Abrade using fine grit abrasives. 3. Wipe with isopropyl alcohol.* Glass 1. Solvent wipe surface using acetone or MEK.* *Note: When using solvents, extinguish all ignition sources, including pilot lights, and follow manufacturer's precautions and directions for use. 7 3MTM Scotch-WeldTM Epoxy Adhesive DP100 Plus Clear Storage and Shelf Life Store 3MTM Scotch-WeldTM Epoxy Adhesive DP100 Plus Clear at 60-80F (1527C) for maximum shelf life. These epoxy adhesive products have a shelf life of 2 years in their unopened containers and 15 months in Duo-Pak containers. Product shelf life is based on date of shipment. Precautionary Information Refer to Product Label and Material Safety Data Sheet for health and safety information before using this product. For additional health and safety information, call 1-800-364-3577 or (651) 737-6501. Technical Information The technical information, recommendations and other statements contained in this document are based upon tests or experience that 3M believes are reliable, but the accuracy or completeness of such information is not guaranteed. Product Use Many factors beyond 3M's control and uniquely within user's knowledge and control can affect the use and performance of a 3M product in a particular application. Given the variety of factors that can affect the use and performance of a 3M product, user is solely responsible for evaluating the 3M product and determining whether it is fit for a particular purpose and suitable for user's method of application. Warranty, Limited Remedy, and Disclaimer Unless an additional warranty is specifically stated on the applicable 3M product packaging or product literature, 3M warrants that each 3M product meets the applicable 3M product specification at the time 3M ships the product. 3M MAKES NO OTHER WARRANTIES OR CONDITIONS, EXPRESS OR IMPLIED, INCLUDING, BUT NOT LIMITED TO, ANY IMPLIED WARRANTY OR CONDITION OF MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE OR ANY IMPLIED WARRANTY OR CONDITION ARISING OUT OF A COURSE OF DEALING, CUSTOM OR USAGE OF TRADE. If the 3M product does not conform to this warranty, then the sole and exclusive remedy is, at 3M's option, replacement of the 3M product or refund of the purchase price. Limitation of Liability Except where prohibited by law, 3M will not be liable for any loss or damage arising from the 3M product, whether direct, indirect, special, incidental or consequential, regardless of the legal theory asserted, including warranty, contract, negligence or strict liability. ISO 9001: 2000 This Industrial Adhesives and Tapes Division product was manufactured under a 3M quality system registered to ISO 9001: 2000 standards. Industrial Adhesives and Tapes Division 3M Center, Building 225-3S-06 St. Paul, MN 55144-1000 800-362-3550 * 877-369-2923 (Fax) www.3M.com/structuraladhesives 3M and Scotch-Weld are trademarks of 3M Company. (c)3M 2016 ( 9 / 2 0 1 6 ) 78-6900-9892-2 8